| Group Spec |
Property |
Unit |
Test method |
Type |
Grade NE2740 DAM |
Grade NE2740 50% R.H. |
Grade NE6040-ST DAM |
Grade NE6040-ST 50% R.H. |
Grade NF3020 DAM |
Grade NF3020 50% R.H. |
Grade NF3040 DAM |
Grade NF3040 50% R.H.
|
|
Description
|
|
|
|
|
Injection Grade, 4% Nano Clay
|
Injection Grade, 4% Nano Clay
|
Super Tough Grade, 4% Nano Clay
|
Super Tough Grade, 4% Nano Clay
|
Film Grade, 2% Nano Clay
|
Film Grade, 2% Nano Clay
|
Film Grade, 4% Nano Clay
|
Film Grade, 4% Nano Clay
|
|
Physical
|
Density
|
g/cm³
|
ASTM D792
|
CRESS-ALON™ A Nano
|
1.15
|
|
|
|
1.14
|
|
1.15
|
|
|
Physical
|
Water Absorption (24 hrs. in 73 °F water)
|
%
|
ASTM D570
|
CRESS-ALON™ A Nano
|
|
|
|
|
0.9
|
|
|
|
|
Physical
|
Relative Viscosity (96% H2SO4, 77 °F)
|
|
|
CRESS-ALON™ A Nano
|
|
|
|
|
|
|
|
|
|
Physical
|
Moisture Content
|
ppm
|
|
CRESS-ALON™ A Nano
|
|
|
|
|
|
|
|
|
|
Physical
|
Extractable
|
weight %
|
|
CRESS-ALON™ A Nano
|
|
|
|
|
|
|
|
|
|
Physical
|
Ash Content (1202 °F)
|
%
|
|
CRESS-ALON™ A Nano
|
|
|
|
|
|
|
|
|
|
Mechanical
|
Tensile Strength at Yield (73 °F)
|
psi
|
ASTM D638
|
CRESS-ALON™ A Nano
|
14,935
|
13,920
|
6,800
|
7,000
|
14,500
|
13,050
|
|
|
|
Mechanical
|
Tensile Strength at Break (73 °F)
|
psi
|
ASTM D638
|
CRESS-ALON™ A Nano
|
14,935
|
13,920
|
|
|
|
|
16,100
|
13,600
|
|
Mechanical
|
Tensile Strain at Yield (73 °F)
|
psi
|
ASTM D638
|
CRESS-ALON™ A Nano
|
|
|
|
|
|
|
|
|
|
Mechanical
|
Tensile Strain at Break (73 °F)
|
psi
|
ASTM D638
|
CRESS-ALON™ A Nano
|
|
|
|
|
|
|
|
|
|
Mechanical
|
Tensile Elongation (73 °F)
|
%
|
ASTM D638
|
CRESS-ALON™ A Nano
|
1.4
|
2.4
|
71
|
182
|
50
|
80
|
3.2
|
2.4
|
|
Mechanical
|
Tensile Modulus (73 °F)
|
psi
|
ASTM D638
|
CRESS-ALON™ A Nano
|
|
|
|
|
580,000
|
493,000
|
726,200
|
580,900
|
|
Mechanical
|
Flexural Strength (73 °F)
|
psi
|
ASTM D790
|
CRESS-ALON™ A Nano
|
23,635
|
20,735
|
|
|
21,025
|
16,965
|
22,500
|
21,100
|
|
Mechanical
|
Flexural Modulus (73 °F)
|
psi
|
ASTM D790
|
CRESS-ALON™ A Nano
|
|
|
319,000
|
276,000
|
565,500
|
435,000
|
610,000
|
552,000
|
|
Mechanical
|
Izod Impact Strength - Notched (73 °F)
|
ft·lb/in
|
ASTM D256
|
CRESS-ALON™ A Nano
|
0.56
|
0.71
|
16
|
20
|
0.50
|
0.52
|
|
|
|
Mechanical
|
Izod Impact Strength - Notched (-4 °F)
|
ft·lb/in
|
ASTM D256
|
CRESS-ALON™ A Nano
|
|
|
|
15.6
|
|
|
|
|
|
Mechanical
|
Izod Impact Strength - Notched (-22 °F)
|
ft·lb/in
|
ASTM D256
|
CRESS-ALON™ A Nano
|
|
|
|
|
|
|
|
|
|
Mechanical
|
Izod Impact Strength - Notched (-40 °F)
|
ft·lb/in
|
ASTM D256
|
CRESS-ALON™ A Nano
|
|
|
5
|
5
|
|
|
|
|
|
Mechanical
|
Rockwell Hardness (R scale)
|
R scale
|
ASTM D785
|
CRESS-ALON™ A Nano
|
|
|
|
|
|
|
|
|
|
Mechanical
|
Rockwell Hardness (Shore D scale)
|
D scale
|
ASTM D785
|
CRESS-ALON™ A Nano
|
|
|
|
|
|
|
|
|
|
Mechanical
|
Rockwell Hardness (M scale)
|
M scale
|
ASTM D785
|
CRESS-ALON™ A Nano
|
|
|
|
|
|
|
|
|
|
Thermal
|
Melting Point
|
°F
|
DSC
|
CRESS-ALON™ A Nano
|
430
|
|
428
|
|
430
|
|
430
|
|
|
Thermal
|
Heat Deflection Temperature - 264 psi
|
°F
|
ASTM D648
|
CRESS-ALON™ A Nano
|
279
|
266
|
177
|
|
266
|
|
297
|
|
|
Thermal
|
Heat Deflection Temperature - 66 psi
|
°F
|
ASTM D648
|
CRESS-ALON™ A Nano
|
|
|
|
|
|
|
|
|
|
Thermal
|
Melt Flow Index at 230 °C, 2.16 kg
|
g/10 min.
|
ASTM D1236
|
CRESS-ALON™ A Nano
|
48.3
|
|
|
|
|
|
|
|
|
Thermal
|
Melt Flow Index at 230 °C, 5.0 kg
|
g/10 min.
|
ASTM D1236
|
CRESS-ALON™ A Nano
|
|
|
|
|
15
|
|
8.9
|
|
|
Thermal
|
Flammability
|
-
|
UL94
|
CRESS-ALON™ A Nano
|
|
|
|
|
|
|
|
|
|
Electrical
|
Volume Resistivity
|
Ω·cm
|
ASTM D257
|
CRESS-ALON™ A Nano
|
|
|
|
|
|
|
|
|
|
Electrical
|
Surface Resistivity
|
Ω
|
ASTM D257
|
CRESS-ALON™ A Nano
|
|
|
|
|
|
|
|
|
|
Moldability
|
Mold Shrinkage - Flow direction
|
%
|
ASTM D955
|
CRESS-ALON™ A Nano
|
|
|
|
|
|
|
|
|
|
Moldability
|
Mold Shrinkage - Transverse direction
|
%
|
ASTM D955
|
CRESS-ALON™ A Nano
|
|
|
|
|
|
|
|
|
|